English translation for "transparent glaze"
|
- 透明釉
Related Translations:
- Example Sentences:
| 1. | This is a chrome green colour stain which develops especially well in glazes containing little or no zinc or magnesium . transparent glazes favour the development of the colour
铬绿色料在少含或不含锌、镁的釉中呈色特别好。透明釉有利于发色效果。 | | 2. | To get the black underglaze , the bisque was first coated with white slip with ornamental lines in black paint and then sharp tools were used to outline the patterns features . sometimes a whittling technique would be employed to expose the white bisque . the piece was subsequently coated with transparent glaze and fired in the kiln , thus creating a sharp contrast between the black and the white
釉下黑彩划花，是先在成形的坯上抹上白化妆土，再用黑彩于化妆土上绘画纹样，再用利器勾划轮廓，有些甚至加以削剔，使黑彩下的白化妆土重现，然后再施透明釉，及入烧制。 | | 3. | The imported transparent glaze fired at lower temperature was analysed semi - quantitatively by adopting emission spectroscope . the stripping of lead and cadmium from this transparent glaze fired at lower temperature in ceramic product was determined by atomic absorption spectroscope . the effect of chemical composition on the stripping of lead and cadmium was analysed . upon the author s opinion , the overproof lead stripping from the imported transparent glaze fired at lower temperature can only be settled by adopting lead - free glaze instead of adopting low - lead prescription . the author succeeded in developing an excellent lead - free transparent glaze fired at the lower temperature of 1000 1050 . the success is based on an inquiry into the feasibility of using such new agents of fusion as li2o and sro in replacement of pbo ; and on a study of the effects of the contents of sio2 ， al2o3 ， b2o3and other metallic oxides on such performances of glaze as coefficient of linear expansion , fusion temperature and transparency . it is also based on an analysis of coefficient of linear expansion of blank and glaze on an analysis of coefficient of linear expansion of blank and glaze on their correlation ; and on a study of technology for preparing glaze
采用发射光谱仪对进口低温透明釉进行半定量分析，并用原子吸收光谱仪测定其陶瓷制品的铅、镉的溶出量，分析化学成分对铅、镉溶出量的影响.结果表明,进口低温透明釉采用低铅配方不能解决铅溶出量的超标问题，只有采用无铅釉才能解决.探讨用氧化锂和氧化锶等新型熔剂完全代替氧化铅的工艺，研究釉料中氧化硅、氧化铝、氧化硼和各种金属氧化物的含量,对釉的线膨胀系数、熔融温度和透明度等性能的影响.分析坯料、釉料的线膨胀系数及其相互关系和釉料制备的工艺，研制出优质的1000 1050低温无铅透明釉 |
- Similar Words：
- "transparent gateway" English translation, "transparent glass" English translation, "transparent glass ceramics" English translation, "transparent glass fibre" English translation, "transparent glass plate" English translation, "transparent glazed paper" English translation, "transparent graph paper" English translation, "transparent grating" English translation, "transparent green" English translation, "transparent hatchetfish" English translation
|
|
|